Corrosion Classification, Rate And Corrosion Product Type: A Review
Main Article Content
Abstract
Corrosion is a slow process that occurs primarily on metal surfaces, but the corrosion related losses are of high order. When considering only the loss of metal, the damages cannot be measured. Except for the least active noble metals, corrosion occurs with all metals. The indirect losses are much higher. Consideration must also be given to the cost of fabrication and cost of preventing corrosion. Indirect losses are higher than the direct losses. When a structure such as building or bridge collapsed due to problems with corrosion the damage often involves the loss of human life and property and the cost of subsequent reconstruction and alternative solution. Corrosion is quite noticeable in some types of corrosion and is only seen when an accident occurs.
Downloads
Article Details
This work is licensed under a Creative Commons Attribution 4.0 International License.
References
Woodtli, J., & Kieselbach, R. (2000). Damage due to hydrogen embrittlement and stress corrosion cracking. Engineering failure analysis, 7(6), 427-450.
Nakamura, S. I., & Suzumura, K. (2009). Hydrogen embrittlement and corrosion fatigue of corroded bridge wires. Journal of Constructional Steel Research, 65(2), 269-277.
Evans, U. R. (1925). Oxygen Distribution as a Factor in the Corrosion of Metals. Industrial & Engineering Chemistry, 17(4), 363-372.
Whitman, W. G., & Russell, R. P. (1925). The Acid Corrosion of Metals. Effect of Oxygen and Velocity. Industrial & Engineering Chemistry, 17(4), 348-354.
Brasunas, A. D. S. (1953). Liquid metal corrosion. Corrosion, 9(3), 78-84.
Iverson, W. P. (1987). Microbial corrosion of metals. Advances in applied microbiology, 32, 1-36.
Lynes, W. (1956). The oxygen concentration cell as a factor in the localized corrosion of metals. Journal of the Electrochemical Society, 103(8), 467.
Crolet, J. L. (1993). Mechanisms of uniform corrosion under corrosion deposits. Journal of materials science, 28, 2589-2606.
Zhang, X. G. (2011). Galvanic corrosion. Uhlig's Corrosion Handbook, 51, 123.
Betts, A. J., & Boulton, L. H. (1993). Crevice corrosion: review of mechanisms, modelling, and mitigation. British corrosion journal, 28(4), 279-296.
Frankel, G. S. (2003). Pitting corrosion. ASM handbook, 13, 236-241.
Burstein, G. T., Liu, C., Souto, R. M., & Vines, S. P. (2004). Origins of pitting corrosion. Corrosion Engineering, Science and Technology, 39(1), 25-30.
Sieradzki, K., & Newman, R. C. (1987). Stress-corrosion cracking. Journal of physics and chemistry of solids, 48(11), 1101-1113.
Phull, B. (2003). Evaluating intergranular corrosion.
Matula, M., Hyspecka, L., Svoboda, M., Vodarek, V., Dagbert, C., Galland, J., ... & Tuma, L. (2001). Intergranular corrosion of AISI 316L steel. Materials characterization, 46(2-3), 203-210.
Li, J., Li, D., Xu, Z., Liao, C., Liu, Y., & Zhong, B. (2018). Selective leaching of valuable metals from laterite nickel ore with ammonium chloride-hydrochloric acid solution. Journal of Cleaner Production, 179, 24-30.
Bermúdez, M. D., Carrión, F. J., Martínez-Nicolás, G., & López, R. (2005). Erosion–corrosion of stainless steels, titanium, tantalum and zirconium. Wear, 258(1-4), 693-700.
Djukic, M. B., Zeravcic, V. S., Bakic, G. M., Sedmak, A., & Rajicic, B. (2015). Hydrogen damage of steels: A case study and hydrogen embrittlement model. Engineering Failure Analysis, 58, 485-498.
Esaklul, K. A. (2017). Hydrogen damage. Trends in Oil and Gas Corrosion Research and Technologies, 315-340.
Wasim, M., Shoaib, S., Mubarak, N. M., Inamuddin, & Asiri, A. M. (2018). Factors influencing corrosion of metal pipes in soils. Environmental Chemistry Letters, 16, 861-879.